X-ray photoelectron spectroscopy of sodium aluminosilicate glasses

Y. Miura, S. Matsumoto, T. Nanba, T. Akazawa

Research output: Contribution to journalArticle

19 Citations (Scopus)

Abstract

X-ray photoelectron spectra of Na2O-Al2O3-SiO2 glasses were measured by a monochromatised Al-Kα XPS instrument with a novel charge control method. Chemical shifts of core level photoelectron spectra of the glass constituent ions were investigated with glass composition with respect to the external energy reference of Au 4f7/2. Peaks at higher and lower energy sides of the O1s signal were observed and they were ascribed to bridging oxide (BO) and nonbridging oxide (NBO) components, respectively. The BO component was successfully separated into two parts: Si-O-Si (BO(1)) and Al-O-Si (BO(2)). The compositional change for the relative amount of the three Ols components follows an equation derived from an assumption that all aluminium ions were four-coordinated. The Nals signal could not be separated into two components of Na+ ions associated with [AlO4/2]- tetrahedra and NBOs. However, the Nals chemical shift reflected the change in the bonding characteristics of Na+ ions in the glasses.

Original languageEnglish
Pages (from-to)24-31
Number of pages8
JournalPhysics and Chemistry of Glasses
Volume41
Issue number1
Publication statusPublished - Dec 1 2000

ASJC Scopus subject areas

  • Ceramics and Composites
  • Physical and Theoretical Chemistry

Fingerprint Dive into the research topics of 'X-ray photoelectron spectroscopy of sodium aluminosilicate glasses'. Together they form a unique fingerprint.

  • Cite this