The Formation Process of the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System

Hiroyuki Ito, Yasunori Ikeda, Zenji Hiroi, Mikio Takano, Yoshichika Bando, Jun Takada, Toshio Egi, Hitoshi Kitaguchi, Kiichi Oda

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

The formation process of the 37Å (high-Tc) phase in the Bi-Pb-Sr-Ca -Cu-O system has been studied for a nominal composition Bi:Pb:Sr:Ca:Cu=0.9: 0.2:1:1:1.6. From this composition we obtained the high-Tc phase crystallizing homogeneously in the Pb-induced modulation mode as reported previously. The solid phases formed after each firing treatment at above 795°C were identified, and the melting points of various combinations of these were measured. As a result, the lowest liquid formation temperature was found to be 825°C for a combination of the 24Å phase and Ca2PbO4. The liquid formation and formation of the Pb-substituted 30Å phase seems to be the initial step the formation of the 37Å phase.

Original languageEnglish
Pages (from-to)743-746
Number of pages4
JournalJournal of the Japan Society of Powder and Powder Metallurgy
Volume37
Issue number5
DOIs
Publication statusPublished - Jan 1 1990

ASJC Scopus subject areas

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'The Formation Process of the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System'. Together they form a unique fingerprint.

  • Cite this

    Ito, H., Ikeda, Y., Hiroi, Z., Takano, M., Bando, Y., Takada, J., Egi, T., Kitaguchi, H., & Oda, K. (1990). The Formation Process of the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System. Journal of the Japan Society of Powder and Powder Metallurgy, 37(5), 743-746. https://doi.org/10.2497/jjspm.37.743