Superconducting Properties of Silver-sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes

Egi Toshio; Mori Naoyuki; Hosotani Katsunori; Nanba Tokuro; Takada Jun

doi:10.2497/jjspm.39.404

Superconducting Properties of Silver-sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes

Egi Toshio, Mori Naoyuki, Hosotani Katsunori, Nanba Tokuro, Takada Jun

Research output: Contribution to journal › Article › peer-review

Abstract

The BPSCCO powder with a nominal composition of Bi:Pb:Sr:Ca:Cu=0.96:0.24:1.0:1.1:1.6 prepared by the co-precipitation method was packed into a Ag tube. The tape was fabricated by plastic deformation. Optimized heat treatment conditions for the tape samples have been studied. The critical current density of the tape samples after the 3rd heat treatment was found to depend on the temperature of the 1st heat treatment. The maximum critical current density was 10, 500A/cm² at zero field and 77K in the sample subjected to the 1st heat treatment at 845°C. The impurity phases with a particle size of 5-10μm, such as Ca-Sr-Cu-O and Ca-Sr-Pb-O, were present even in the sample with Jc=10, 500A/cm².

Original language	English
Pages (from-to)	404-407
Number of pages	4
Journal	Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
Volume	39
Issue number	5
DOIs	https://doi.org/10.2497/jjspm.39.404
Publication status	Published - 1992

ASJC Scopus subject areas

Mechanical Engineering
Industrial and Manufacturing Engineering
Metals and Alloys
Materials Chemistry

Access to Document

10.2497/jjspm.39.404

Fingerprint Dive into the research topics of 'Superconducting Properties of Silver-sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes'. Together they form a unique fingerprint.

Cite this

@article{c25dbbc774e043a1812eb8d285536f7c,

title = "Superconducting Properties of Silver-sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes",

abstract = "The BPSCCO powder with a nominal composition of Bi:Pb:Sr:Ca:Cu=0.96:0.24:1.0:1.1:1.6 prepared by the co-precipitation method was packed into a Ag tube. The tape was fabricated by plastic deformation. Optimized heat treatment conditions for the tape samples have been studied. The critical current density of the tape samples after the 3rd heat treatment was found to depend on the temperature of the 1st heat treatment. The maximum critical current density was 10, 500A/cm2 at zero field and 77K in the sample subjected to the 1st heat treatment at 845°C. The impurity phases with a particle size of 5-10μm, such as Ca-Sr-Cu-O and Ca-Sr-Pb-O, were present even in the sample with Jc=10, 500A/cm2.",

author = "Egi Toshio and Mori Naoyuki and Hosotani Katsunori and Nanba Tokuro and Takada Jun",

year = "1992",

doi = "10.2497/jjspm.39.404",

language = "English",

volume = "39",

pages = "404--407",

journal = "Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy",

issn = "0532-8799",

publisher = "Funtai Funamtsu Yakin Kyokai/Japan Soc. of Powder Metallurgy",

number = "5",

}

TY - JOUR

T1 - Superconducting Properties of Silver-sheathed Bi-Pb-Sr-Ca-Cu-O Superconducting Tapes

AU - Toshio, Egi

AU - Naoyuki, Mori

AU - Katsunori, Hosotani

AU - Tokuro, Nanba

AU - Jun, Takada

PY - 1992

Y1 - 1992

N2 - The BPSCCO powder with a nominal composition of Bi:Pb:Sr:Ca:Cu=0.96:0.24:1.0:1.1:1.6 prepared by the co-precipitation method was packed into a Ag tube. The tape was fabricated by plastic deformation. Optimized heat treatment conditions for the tape samples have been studied. The critical current density of the tape samples after the 3rd heat treatment was found to depend on the temperature of the 1st heat treatment. The maximum critical current density was 10, 500A/cm2 at zero field and 77K in the sample subjected to the 1st heat treatment at 845°C. The impurity phases with a particle size of 5-10μm, such as Ca-Sr-Cu-O and Ca-Sr-Pb-O, were present even in the sample with Jc=10, 500A/cm2.

AB - The BPSCCO powder with a nominal composition of Bi:Pb:Sr:Ca:Cu=0.96:0.24:1.0:1.1:1.6 prepared by the co-precipitation method was packed into a Ag tube. The tape was fabricated by plastic deformation. Optimized heat treatment conditions for the tape samples have been studied. The critical current density of the tape samples after the 3rd heat treatment was found to depend on the temperature of the 1st heat treatment. The maximum critical current density was 10, 500A/cm2 at zero field and 77K in the sample subjected to the 1st heat treatment at 845°C. The impurity phases with a particle size of 5-10μm, such as Ca-Sr-Cu-O and Ca-Sr-Pb-O, were present even in the sample with Jc=10, 500A/cm2.

UR - http://www.scopus.com/inward/record.url?scp=85004357669&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85004357669&partnerID=8YFLogxK

U2 - 10.2497/jjspm.39.404

DO - 10.2497/jjspm.39.404

M3 - Article

AN - SCOPUS:85004357669

VL - 39

SP - 404

EP - 407

JO - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

JF - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

SN - 0532-8799

IS - 5

ER -