Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature

Takashi Katahira, Takeshi Uemori, Tetsuya Yoshida, Michihiro Takiguchi, Tetsuo Naka, Komgrit Lawanwong, Fusahito Yoshida

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

In recent years, warm forming of magnesium sheets has been investigated by many researchers since the ductility of the sheets becomes considerably higher due to low CRSS (critical resolved shear stress) at high temperatures (e.g., [1]-[3]). In the present research, the springback of AZ31 magnesium sheet was investigated by performing a draw-bending experiment at several temperatures from 20 °C (room temperature) to 200 °C at drawing speeds ranging from 0.01 to 1.0 mm/s. From the experiment, it was found that the springback was remarkably reduced at 200 °C, especially at a low forming speed, since the flow stress was very low under such a forming condition, and furthermore, the stress relaxation effect was dominant. The effects of temperature and forming speed on springback were discussed.

Original languageEnglish
Title of host publicationAdvances in Engineering Plasticity and its Application IX
EditorsJeong Whan Yoon, Young-Suk Kim, Heung Nam Han, Beom Soo Kang
PublisherTrans Tech Publications Ltd
Pages127-132
Number of pages6
ISBN (Print)9783035713626
DOIs
Publication statusPublished - Jan 1 2019
Event14th Asia-Pacific Symposium on Engineering Plasticity and its Applications, AEPA 2018 - Seogwipo-si, Korea, Republic of
Duration: Dec 2 2018Dec 7 2018

Publication series

NameKey Engineering Materials
Volume794 KEM
ISSN (Print)1013-9826

Conference

Conference14th Asia-Pacific Symposium on Engineering Plasticity and its Applications, AEPA 2018
CountryKorea, Republic of
CitySeogwipo-si
Period12/2/1812/7/18

Fingerprint

Magnesium alloys
Magnesium
Temperature
Stress relaxation
Plastic flow
Ductility
Shear stress
Experiments

Keywords

  • AZ31 magnesium sheet
  • Draw bending
  • Springback
  • Warm forming

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Katahira, T., Uemori, T., Yoshida, T., Takiguchi, M., Naka, T., Lawanwong, K., & Yoshida, F. (2019). Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature. In J. W. Yoon, Y-S. Kim, H. N. Han, & B. S. Kang (Eds.), Advances in Engineering Plasticity and its Application IX (pp. 127-132). (Key Engineering Materials; Vol. 794 KEM). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.794.127

Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature. / Katahira, Takashi; Uemori, Takeshi; Yoshida, Tetsuya; Takiguchi, Michihiro; Naka, Tetsuo; Lawanwong, Komgrit; Yoshida, Fusahito.

Advances in Engineering Plasticity and its Application IX. ed. / Jeong Whan Yoon; Young-Suk Kim; Heung Nam Han; Beom Soo Kang. Trans Tech Publications Ltd, 2019. p. 127-132 (Key Engineering Materials; Vol. 794 KEM).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Katahira, T, Uemori, T, Yoshida, T, Takiguchi, M, Naka, T, Lawanwong, K & Yoshida, F 2019, Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature. in JW Yoon, Y-S Kim, HN Han & BS Kang (eds), Advances in Engineering Plasticity and its Application IX. Key Engineering Materials, vol. 794 KEM, Trans Tech Publications Ltd, pp. 127-132, 14th Asia-Pacific Symposium on Engineering Plasticity and its Applications, AEPA 2018, Seogwipo-si, Korea, Republic of, 12/2/18. https://doi.org/10.4028/www.scientific.net/KEM.794.127
Katahira T, Uemori T, Yoshida T, Takiguchi M, Naka T, Lawanwong K et al. Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature. In Yoon JW, Kim Y-S, Han HN, Kang BS, editors, Advances in Engineering Plasticity and its Application IX. Trans Tech Publications Ltd. 2019. p. 127-132. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.794.127
Katahira, Takashi ; Uemori, Takeshi ; Yoshida, Tetsuya ; Takiguchi, Michihiro ; Naka, Tetsuo ; Lawanwong, Komgrit ; Yoshida, Fusahito. / Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature. Advances in Engineering Plasticity and its Application IX. editor / Jeong Whan Yoon ; Young-Suk Kim ; Heung Nam Han ; Beom Soo Kang. Trans Tech Publications Ltd, 2019. pp. 127-132 (Key Engineering Materials).
@inproceedings{0f481033a3c8474fa03382c4cdee2b7c,
title = "Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature",
abstract = "In recent years, warm forming of magnesium sheets has been investigated by many researchers since the ductility of the sheets becomes considerably higher due to low CRSS (critical resolved shear stress) at high temperatures (e.g., [1]-[3]). In the present research, the springback of AZ31 magnesium sheet was investigated by performing a draw-bending experiment at several temperatures from 20 °C (room temperature) to 200 °C at drawing speeds ranging from 0.01 to 1.0 mm/s. From the experiment, it was found that the springback was remarkably reduced at 200 °C, especially at a low forming speed, since the flow stress was very low under such a forming condition, and furthermore, the stress relaxation effect was dominant. The effects of temperature and forming speed on springback were discussed.",
keywords = "AZ31 magnesium sheet, Draw bending, Springback, Warm forming",
author = "Takashi Katahira and Takeshi Uemori and Tetsuya Yoshida and Michihiro Takiguchi and Tetsuo Naka and Komgrit Lawanwong and Fusahito Yoshida",
year = "2019",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/KEM.794.127",
language = "English",
isbn = "9783035713626",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "127--132",
editor = "Yoon, {Jeong Whan} and Young-Suk Kim and Han, {Heung Nam} and Kang, {Beom Soo}",
booktitle = "Advances in Engineering Plasticity and its Application IX",

}

TY - GEN

T1 - Springback suppression of AZ31 magnesium alloy sheet in draw bending at elevated temperature

AU - Katahira, Takashi

AU - Uemori, Takeshi

AU - Yoshida, Tetsuya

AU - Takiguchi, Michihiro

AU - Naka, Tetsuo

AU - Lawanwong, Komgrit

AU - Yoshida, Fusahito

PY - 2019/1/1

Y1 - 2019/1/1

N2 - In recent years, warm forming of magnesium sheets has been investigated by many researchers since the ductility of the sheets becomes considerably higher due to low CRSS (critical resolved shear stress) at high temperatures (e.g., [1]-[3]). In the present research, the springback of AZ31 magnesium sheet was investigated by performing a draw-bending experiment at several temperatures from 20 °C (room temperature) to 200 °C at drawing speeds ranging from 0.01 to 1.0 mm/s. From the experiment, it was found that the springback was remarkably reduced at 200 °C, especially at a low forming speed, since the flow stress was very low under such a forming condition, and furthermore, the stress relaxation effect was dominant. The effects of temperature and forming speed on springback were discussed.

AB - In recent years, warm forming of magnesium sheets has been investigated by many researchers since the ductility of the sheets becomes considerably higher due to low CRSS (critical resolved shear stress) at high temperatures (e.g., [1]-[3]). In the present research, the springback of AZ31 magnesium sheet was investigated by performing a draw-bending experiment at several temperatures from 20 °C (room temperature) to 200 °C at drawing speeds ranging from 0.01 to 1.0 mm/s. From the experiment, it was found that the springback was remarkably reduced at 200 °C, especially at a low forming speed, since the flow stress was very low under such a forming condition, and furthermore, the stress relaxation effect was dominant. The effects of temperature and forming speed on springback were discussed.

KW - AZ31 magnesium sheet

KW - Draw bending

KW - Springback

KW - Warm forming

UR - http://www.scopus.com/inward/record.url?scp=85067869067&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85067869067&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.794.127

DO - 10.4028/www.scientific.net/KEM.794.127

M3 - Conference contribution

AN - SCOPUS:85067869067

SN - 9783035713626

T3 - Key Engineering Materials

SP - 127

EP - 132

BT - Advances in Engineering Plasticity and its Application IX

A2 - Yoon, Jeong Whan

A2 - Kim, Young-Suk

A2 - Han, Heung Nam

A2 - Kang, Beom Soo

PB - Trans Tech Publications Ltd

ER -