Scanning probe microscopic observation of a surface precipitation of Mg-6 mass%Al alloy

Moritaka Hida, Koichi Imada, Akira Sakakibara, Yoshito Takemoto

Research output: Contribution to journalArticle

Abstract

Surface and interior precipitations of Mg-6 mass%Al alloy were morphologically studied by SPM observation with AFM and KFM modes, TEM and XRD methods. The hardness increment due to the precipitation was negligibly small. According to AFM contrast the precipitates on the surface were identified as droplet-like particles (1∼4 μ4); on the other hand the ones formed in the alloy as needle-like (∼1 μm). It was confirmed by XRD that both types of the precipitates had γ-structure (Al12Mg17), and the peak height of the surface precipitates was about 3 times as high as that of the interior ones. The droplet-like precipitates projecting from the surface had a higher KFM electric potential than that of the matrix solid solution, however the precipitates embedded in either the surface layer or the matrix had a lower KFM electric potential.

Original languageEnglish
Pages (from-to)126-130
Number of pages5
JournalKeikinzoku/Journal of Japan Institute of Light Metals
Volume52
Issue number3
Publication statusPublished - Mar 2002

Fingerprint

Precipitates
Scanning
Electric potential
Needles
Solid solutions
Hardness
Transmission electron microscopy

Keywords

  • Al-Mg alloy
  • Atomic force microscope
  • Kelvin force microscope
  • Surface precipitation

ASJC Scopus subject areas

  • Metals and Alloys

Cite this

Scanning probe microscopic observation of a surface precipitation of Mg-6 mass%Al alloy. / Hida, Moritaka; Imada, Koichi; Sakakibara, Akira; Takemoto, Yoshito.

In: Keikinzoku/Journal of Japan Institute of Light Metals, Vol. 52, No. 3, 03.2002, p. 126-130.

Research output: Contribution to journalArticle

@article{8024bed0eb9c455e8724600bd911c10a,
title = "Scanning probe microscopic observation of a surface precipitation of Mg-6 mass{\%}Al alloy",
abstract = "Surface and interior precipitations of Mg-6 mass{\%}Al alloy were morphologically studied by SPM observation with AFM and KFM modes, TEM and XRD methods. The hardness increment due to the precipitation was negligibly small. According to AFM contrast the precipitates on the surface were identified as droplet-like particles (1∼4 μ4); on the other hand the ones formed in the alloy as needle-like (∼1 μm). It was confirmed by XRD that both types of the precipitates had γ-structure (Al12Mg17), and the peak height of the surface precipitates was about 3 times as high as that of the interior ones. The droplet-like precipitates projecting from the surface had a higher KFM electric potential than that of the matrix solid solution, however the precipitates embedded in either the surface layer or the matrix had a lower KFM electric potential.",
keywords = "Al-Mg alloy, Atomic force microscope, Kelvin force microscope, Surface precipitation",
author = "Moritaka Hida and Koichi Imada and Akira Sakakibara and Yoshito Takemoto",
year = "2002",
month = "3",
language = "English",
volume = "52",
pages = "126--130",
journal = "Keikinzoku/Journal of Japan Institute of Light Metals",
issn = "0451-5994",
publisher = "Keikinzoku Gakkai/Japan Institute of Light Metals",
number = "3",

}

TY - JOUR

T1 - Scanning probe microscopic observation of a surface precipitation of Mg-6 mass%Al alloy

AU - Hida, Moritaka

AU - Imada, Koichi

AU - Sakakibara, Akira

AU - Takemoto, Yoshito

PY - 2002/3

Y1 - 2002/3

N2 - Surface and interior precipitations of Mg-6 mass%Al alloy were morphologically studied by SPM observation with AFM and KFM modes, TEM and XRD methods. The hardness increment due to the precipitation was negligibly small. According to AFM contrast the precipitates on the surface were identified as droplet-like particles (1∼4 μ4); on the other hand the ones formed in the alloy as needle-like (∼1 μm). It was confirmed by XRD that both types of the precipitates had γ-structure (Al12Mg17), and the peak height of the surface precipitates was about 3 times as high as that of the interior ones. The droplet-like precipitates projecting from the surface had a higher KFM electric potential than that of the matrix solid solution, however the precipitates embedded in either the surface layer or the matrix had a lower KFM electric potential.

AB - Surface and interior precipitations of Mg-6 mass%Al alloy were morphologically studied by SPM observation with AFM and KFM modes, TEM and XRD methods. The hardness increment due to the precipitation was negligibly small. According to AFM contrast the precipitates on the surface were identified as droplet-like particles (1∼4 μ4); on the other hand the ones formed in the alloy as needle-like (∼1 μm). It was confirmed by XRD that both types of the precipitates had γ-structure (Al12Mg17), and the peak height of the surface precipitates was about 3 times as high as that of the interior ones. The droplet-like precipitates projecting from the surface had a higher KFM electric potential than that of the matrix solid solution, however the precipitates embedded in either the surface layer or the matrix had a lower KFM electric potential.

KW - Al-Mg alloy

KW - Atomic force microscope

KW - Kelvin force microscope

KW - Surface precipitation

UR - http://www.scopus.com/inward/record.url?scp=0036501751&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0036501751&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0036501751

VL - 52

SP - 126

EP - 130

JO - Keikinzoku/Journal of Japan Institute of Light Metals

JF - Keikinzoku/Journal of Japan Institute of Light Metals

SN - 0451-5994

IS - 3

ER -