Rolling contact fatigue of alumina ceramics sprayed roller

Masahiro Fujii, Akira Yoshida, Sadato Shigemura, Kazumi Tani, Kenji Yuki

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

The rolling contact fatigue of a sprayed alumina ceramics with a nominal composition of Al2O32.3 mass%TiO2 was studied with a two-roller test apparatus under pure rolling contact condition with oil lubricant. The alumina ceramics was prepared by plasma spray process. The influence of undercoating of sprayed Ni based alloy and surface sealing on the rolling contact fatigue was investigated. The failure mode of all sprayed rollers was spalling caused by subsurface cracking. Neither undercoating nor surface sealing contributed to the improvement of the rolling contact fatigue. The elastic modulus of the alumina sprayed layer evaluated with the nano-indentation method was around 85 GPa. The subsurface shear stresses were calculated with two-dimensional FEM analyses. The maximum values of orthogonal shear stress and maximum shear stress occurred within the spraved layer. The depths of observed subsurface cracks were generally deeper than those of the maxima of shear stresses.

Original languageEnglish
Pages (from-to)3331-3338
Number of pages8
JournalNihon Kikai Gakkai Ronbunshu, C Hen/Transactions of the Japan Society of Mechanical Engineers, Part C
Volume70
Issue number11
DOIs
Publication statusPublished - Nov 2004

Keywords

  • Alumina
  • FEM
  • Machine Element
  • Nano-Indentation
  • Oil Lubrication
  • Rolling Contact Fatigue
  • Spraying
  • Tribology

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

Fingerprint

Dive into the research topics of 'Rolling contact fatigue of alumina ceramics sprayed roller'. Together they form a unique fingerprint.

Cite this