Promotion of H2 production from ethanol steam reforming by zeolite basicity

Hitoshi Inokawa, Shunsuke Nishimoto, Yoshikazu Kameshima, Michihiro Miyake

Research output: Contribution to journalArticle

19 Citations (Scopus)

Abstract

The effect of the basicity of zeolite as a metallic catalyst substrate on ethanol steam reforming reaction was investigated. Catalysts with various basicities were prepared using an ion exchange process with aqueous solutions including Na+, K+ and Cs+ after an impregnation process of Ni on Na-Y zeolite (referred to as Ni/Na-Y, Ni/K-Y and Ni/Cs-Y, respectively). Infrared spectroscopy indicated that the OH bonds of ethanol molecules adsorbed on zeolites were weakened with increasing zeolite basicity. H2 production at 300 °C increased in the order of Ni/Cs-Y > Ni/K-Y > Ni/Na-Y, and selectivity for a high production ratio of H 2 to C2H4 was significantly promoted by exchanging Na+ for K+ or Cs+. H2 production at 500 °C was also enhanced by the zeolite basicity; however, degradation of catalytic activity was mainly caused by carbon deposition on the three samples at this temperature. Ni/Cs-Y, with higher H2 production than Ni/Na-Y, also exhibited higher resistance to carbon deposition. Increase of the zeolite basicity was effective for selective acceleration of the dehydrogenation reaction with ethanol, inhibition of coke deposition, and the promotion of H2 production.

Original languageEnglish
Pages (from-to)15195-15202
Number of pages8
JournalInternational Journal of Hydrogen Energy
Volume36
Issue number23
DOIs
Publication statusPublished - Nov 1 2011

Keywords

  • Alkali metal exchanged zeolite
  • Ethanol steam reforming
  • Hydrogen
  • Zeolite basicity

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology

Fingerprint Dive into the research topics of 'Promotion of H<sub>2</sub> production from ethanol steam reforming by zeolite basicity'. Together they form a unique fingerprint.

  • Cite this