Preparation and properties of CaO-MgO-Al2O3-SiO 2 glass-ceramics from kaolin clay refining waste (Kira) and dolomite

Tomohiro Toya, Yoshihiro Tamura, Yoshikazu Kameshima, Kiyoshi Okada

Research output: Contribution to journalArticle

66 Citations (Scopus)

Abstract

CaO-MgO-Al2O3-SiO2 glass-ceramics were prepared from mixtures of waste generated from refining of kaolin clay (called Kira) and dolomite (CaMg(CO3)2). Kira was mixed with dolomite in mass ratios of 65/35 (sample 1) and 75/25 (sample 2). They were melted at 1350°C and quenched in water to obtain glasses. The quenched glasses were ground to < 100mesh and used to prepare glass-ceramics. Crystallization of the parent glass occurred above 900°C, producing diopside (CaMgSi2O6) and anorthite (CaAl2Si 2O8) as major crystalline phases; diopside > anorthite in sample 1 and anorthite > diopside in sample 2. The macroscopic appearance of the samples changed from transparent pale green glass to smooth-textured shiny white upon crystallization. The four point bending strengths of the as-fired glass-ceramics were 130MPa in sample 1 and 73 MPa in sample 2, which was approximately half of the value for sample 1. Vickers microhardness values were found to be 7.4 and 7.6 GPa in samples 1 and 2, respectively. The thermal expansion coefficients of the glass-ceramics prepared at 1000°C for 1h were 6.7 × 10-6°C-1 (30-380°C) in sample 1 and 4.7 × 10-6°C-1 in sample 2. Since the chemical durability for acid and alkali was excellent in these glass-ceramics, they are considered to be candidates for applications such as building materials, ceramic tiles, etc.

Original languageEnglish
Pages (from-to)983-989
Number of pages7
JournalCeramics International
Volume30
Issue number6
DOIs
Publication statusPublished - Jun 28 2004
Externally publishedYes

Keywords

  • C. Mechanical properties
  • Chemical durability
  • D. Glass-ceramics
  • Dolomite
  • Kaolin clay waste

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Preparation and properties of CaO-MgO-Al<sub>2</sub>O<sub>3</sub>-SiO <sub>2</sub> glass-ceramics from kaolin clay refining waste (Kira) and dolomite'. Together they form a unique fingerprint.

  • Cite this