Photon emission during fracture of carbon materials

K. Yasuda, K. Yamamoto, T. Shiota, Y. Matsuo

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

Photon emission (phE) during fracture was investigated on glass-like carbon, pyrolytic graphite, polycrystalline graphite, and carbon fiber reinforced composites (CC composites). The CC composites were heat treated at 1000, 1500, and 2000 °C. The specimen was fractured by three-point bending and the resulting phE was measured at atmospheric pressure, 10-3 and 10-6 Pa. The phE was not observed on any samples at atmospheric pressure, whereas it occurred on the glass-like carbon and CC composites at 10-3 and 10-6 Pa. The phE intensity at 10-3 Pa was higher than that at 10-6 Pa. This study revealed that the phE on the carbon materials depended on their crystal structure and surrounding gas pressure. The gas pressure dependence suggests that the phE resulted from gas discharge.

Original languageEnglish
Pages (from-to)187-192
Number of pages6
JournalJournal of Vacuum Science and Technology A: Vacuum, Surfaces and Films
Volume27
Issue number2
DOIs
Publication statusPublished - Mar 9 2009
Externally publishedYes

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Fingerprint Dive into the research topics of 'Photon emission during fracture of carbon materials'. Together they form a unique fingerprint.

  • Cite this