Photoluminescence increase of Er3+ in Na2O-Nb2O5-SiO2 glasses after crystallization

Zhidong Yao, Yong Ding, Tokuro Nanba, Yoshinari Miura

Research output: Contribution to journalConference article

4 Citations (Scopus)

Abstract

Photoluminescence (PL) of Er3+ doped in xNaO0.5-xNbO2.5-(100-2x)SiO2 (mol%) (x = 24, 27, 30, 33, 36) glasses was investigated before and after crystallization. After crystallization, Er3+ was determined to be in the glass phase. Following the precipitation of the NaNbO3 crystalline phase in these glasses, PL intensity of 4S3/24I15/2 transition of Er3+ increased. A maximum of >100-fold increment in the PL intensity was observed after crystallization as compared with that of the uncrystallized glass. The mechanism of augmentation of the PL intensity is discussed in terms of the theory of PL intensity. We assume that the difference in the refractive index between the residual glass and crystallized phases was a dominant factor causing the increase of the PL intensity after crystallization.

Original languageEnglish
Pages (from-to)45-50
Number of pages6
JournalJournal of Non-Crystalline Solids
Volume259
Issue number1-3
DOIs
Publication statusPublished - Nov 2 1999
EventProceedings of the 1998 Symposium on Advances in Photonic Glasses - Kyongju, Korea
Duration: Sep 20 1998Sep 23 1998

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Condensed Matter Physics
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Photoluminescence increase of Er<sup>3+</sup> in Na<sub>2</sub>O-Nb<sub>2</sub>O<sub>5</sub>-SiO<sub>2</sub> glasses after crystallization'. Together they form a unique fingerprint.

  • Cite this