Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses

S. Sumimiya, Tokuro Nanba, Y. Miura, Shinichi Sakida

Research output: Chapter in Book/Report/Conference proceedingConference contribution

1 Citation (Scopus)

Abstract

We investigated infrared luminescent phenomena in bismuth lanthanum borate glasses. In bismuth lanthanum borate glasses, the absorption peak was observed at 460 nm. The absorption peak was observed only when the glass was melted in Al2O3 crucible, whereas no peak was seen in the case of Pt crucible and the case of Al2O3 doped sample melted in Pt crucible. The infrared emission peak was observed at 1300 nm excited at 800nm. Life time at 1300 nm was 56.7 μs. We suggested that the absorption and infrared emission have been associated with pentavalent Bi ions in the glasses. It was estimated by La 3d XPS spectra and ESR spectra.

Original languageEnglish
Title of host publicationCeramic Transactions
Pages127-133
Number of pages7
Volume197
Publication statusPublished - 2006
Event6th Pacific Rim Conference on Ceramic and Glass Technology - Maui, Hawaii, United States
Duration: Sep 11 2005Sep 16 2005

Publication series

NameCeramic Transactions
Volume197
ISSN (Print)10421122

Other

Other6th Pacific Rim Conference on Ceramic and Glass Technology
CountryUnited States
CityMaui, Hawaii
Period9/11/059/16/05

Fingerprint

Crucibles
Optical properties
Lanthanum
Glass
Borates
Bismuth
Infrared radiation
Paramagnetic resonance
X ray photoelectron spectroscopy
Ions
boron oxide

ASJC Scopus subject areas

  • Ceramics and Composites

Cite this

Sumimiya, S., Nanba, T., Miura, Y., & Sakida, S. (2006). Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses. In Ceramic Transactions (Vol. 197, pp. 127-133). (Ceramic Transactions; Vol. 197).

Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses. / Sumimiya, S.; Nanba, Tokuro; Miura, Y.; Sakida, Shinichi.

Ceramic Transactions. Vol. 197 2006. p. 127-133 (Ceramic Transactions; Vol. 197).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Sumimiya, S, Nanba, T, Miura, Y & Sakida, S 2006, Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses. in Ceramic Transactions. vol. 197, Ceramic Transactions, vol. 197, pp. 127-133, 6th Pacific Rim Conference on Ceramic and Glass Technology, Maui, Hawaii, United States, 9/11/05.
Sumimiya S, Nanba T, Miura Y, Sakida S. Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses. In Ceramic Transactions. Vol. 197. 2006. p. 127-133. (Ceramic Transactions).
Sumimiya, S. ; Nanba, Tokuro ; Miura, Y. ; Sakida, Shinichi. / Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses. Ceramic Transactions. Vol. 197 2006. pp. 127-133 (Ceramic Transactions).
@inproceedings{891132043cf04affab499fac60de7459,
title = "Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses",
abstract = "We investigated infrared luminescent phenomena in bismuth lanthanum borate glasses. In bismuth lanthanum borate glasses, the absorption peak was observed at 460 nm. The absorption peak was observed only when the glass was melted in Al2O3 crucible, whereas no peak was seen in the case of Pt crucible and the case of Al2O3 doped sample melted in Pt crucible. The infrared emission peak was observed at 1300 nm excited at 800nm. Life time at 1300 nm was 56.7 μs. We suggested that the absorption and infrared emission have been associated with pentavalent Bi ions in the glasses. It was estimated by La 3d XPS spectra and ESR spectra.",
author = "S. Sumimiya and Tokuro Nanba and Y. Miura and Shinichi Sakida",
year = "2006",
language = "English",
isbn = "0470083433",
volume = "197",
series = "Ceramic Transactions",
pages = "127--133",
booktitle = "Ceramic Transactions",

}

TY - GEN

T1 - Optical properties of Bi2O3-La2O 3-Al2O3-B2O3 glasses

AU - Sumimiya, S.

AU - Nanba, Tokuro

AU - Miura, Y.

AU - Sakida, Shinichi

PY - 2006

Y1 - 2006

N2 - We investigated infrared luminescent phenomena in bismuth lanthanum borate glasses. In bismuth lanthanum borate glasses, the absorption peak was observed at 460 nm. The absorption peak was observed only when the glass was melted in Al2O3 crucible, whereas no peak was seen in the case of Pt crucible and the case of Al2O3 doped sample melted in Pt crucible. The infrared emission peak was observed at 1300 nm excited at 800nm. Life time at 1300 nm was 56.7 μs. We suggested that the absorption and infrared emission have been associated with pentavalent Bi ions in the glasses. It was estimated by La 3d XPS spectra and ESR spectra.

AB - We investigated infrared luminescent phenomena in bismuth lanthanum borate glasses. In bismuth lanthanum borate glasses, the absorption peak was observed at 460 nm. The absorption peak was observed only when the glass was melted in Al2O3 crucible, whereas no peak was seen in the case of Pt crucible and the case of Al2O3 doped sample melted in Pt crucible. The infrared emission peak was observed at 1300 nm excited at 800nm. Life time at 1300 nm was 56.7 μs. We suggested that the absorption and infrared emission have been associated with pentavalent Bi ions in the glasses. It was estimated by La 3d XPS spectra and ESR spectra.

UR - http://www.scopus.com/inward/record.url?scp=33751394226&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33751394226&partnerID=8YFLogxK

M3 - Conference contribution

SN - 0470083433

SN - 9780470083437

VL - 197

T3 - Ceramic Transactions

SP - 127

EP - 133

BT - Ceramic Transactions

ER -