Microstructure of Nd-Ga-O3 new seed layer for LPE growth of YBCO film

Seok Beom Kim, Sang Im Yoo, Yasuji Yamada

Research output: Contribution to journalConference article

Abstract

The microstructure and crystallization mechanism of NdGaO3 (NGO) new seed layer for liquid phase epitaxy (LPE) growth of YBa2Cu3O7-δ (YBCO) were revealed using high resolution SEM and TEM. NGO layer deposited by PLD at room temperature shows that very porous and columnar structure and this layer indicated amorphous by x-ray analysis. Amorphous NGO layer was crystallized with good in-plane and out of plane orientations keeping columnar structure by simple post annealing process. Biaxially aligned YBCO thick films were successfully fabricated on oriented novel porous NGO new seed layer. Although many cracks were observed for normally LPE grown YBCO films on NGO(110) single crystalline substrate, it was crack-free formed on porous NGO(100) film.

Original languageEnglish
Pages (from-to)2571-2574
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume13
Issue number2 III
DOIs
Publication statusPublished - Jun 1 2003
Externally publishedYes
Event2002 Applied Superconductivity Conference - Houston, TX, United States
Duration: Aug 4 2002Aug 9 2002

    Fingerprint

Keywords

  • LPE
  • NdGaO
  • PLD
  • YBCO film

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

Cite this