Magnetic-field properties of high critical current density YBCO films deposited by TFA-MOD

Seok Beom Kim, S. Murase, Y. Yamada, T. Araki, I. Hirabayashi

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

The critical current density, Jc, of metal-organic deposition process using trifluoroacetates (TFA-MOD) based YBCO films was measured between 20 K and 77 K in magnetic fields up to 9.5 T as a function of the field direction. C-axis oriented YBCO films was deposited on LaAlO3 single crystalline substrates and also on CeO2 buffered IBAD (YSZ/Hastelloy) substrates by TFA-MOD method. The obtained Jc values at 77 K and 0 T were 7 and 1.7 MA/cm2 for LaAlO3 and IBAD substrates, respectively. High Jc values over 105 A/cm2 were maintained up to 4 T (B//c-axis) for the LaAlO3 substrate and up to 3 T (B//c-axis) for the CeO2 buffered IBAD substrate. These results imply that TFA-MOD with simple fabrication process is very promising for the practical YBCO coated conductor. And the dependences on temperature and angular of the Jc at various external magnetic fields for some different thicknesses YBCO films was reported.

Original languageEnglish
Pages (from-to)2645-2648
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume15
Issue number2 PART III
DOIs
Publication statusPublished - Jun 2005

Fingerprint

critical current
Ion beam assisted deposition
Magnetic fields
current density
Substrates
magnetic fields
Hastelloy (trademark)
Trifluoroacetic Acid
yttria-stabilized zirconia
Film thickness
conductors
Metals
Crystalline materials
Fabrication
fabrication
metals
Temperature
temperature

Keywords

  • Jc - B - θ
  • TFA-MOD
  • Thickness
  • YBCO film

ASJC Scopus subject areas

  • Electrical and Electronic Engineering
  • Physics and Astronomy (miscellaneous)

Cite this

Magnetic-field properties of high critical current density YBCO films deposited by TFA-MOD. / Kim, Seok Beom; Murase, S.; Yamada, Y.; Araki, T.; Hirabayashi, I.

In: IEEE Transactions on Applied Superconductivity, Vol. 15, No. 2 PART III, 06.2005, p. 2645-2648.

Research output: Contribution to journalArticle

Kim, Seok Beom ; Murase, S. ; Yamada, Y. ; Araki, T. ; Hirabayashi, I. / Magnetic-field properties of high critical current density YBCO films deposited by TFA-MOD. In: IEEE Transactions on Applied Superconductivity. 2005 ; Vol. 15, No. 2 PART III. pp. 2645-2648.
@article{68fc1f2606a14a0783a04d4ca5538c61,
title = "Magnetic-field properties of high critical current density YBCO films deposited by TFA-MOD",
abstract = "The critical current density, Jc, of metal-organic deposition process using trifluoroacetates (TFA-MOD) based YBCO films was measured between 20 K and 77 K in magnetic fields up to 9.5 T as a function of the field direction. C-axis oriented YBCO films was deposited on LaAlO3 single crystalline substrates and also on CeO2 buffered IBAD (YSZ/Hastelloy) substrates by TFA-MOD method. The obtained Jc values at 77 K and 0 T were 7 and 1.7 MA/cm2 for LaAlO3 and IBAD substrates, respectively. High Jc values over 105 A/cm2 were maintained up to 4 T (B//c-axis) for the LaAlO3 substrate and up to 3 T (B//c-axis) for the CeO2 buffered IBAD substrate. These results imply that TFA-MOD with simple fabrication process is very promising for the practical YBCO coated conductor. And the dependences on temperature and angular of the Jc at various external magnetic fields for some different thicknesses YBCO films was reported.",
keywords = "Jc - B - θ, TFA-MOD, Thickness, YBCO film",
author = "Kim, {Seok Beom} and S. Murase and Y. Yamada and T. Araki and I. Hirabayashi",
year = "2005",
month = "6",
doi = "10.1109/TASC.2005.847757",
language = "English",
volume = "15",
pages = "2645--2648",
journal = "IEEE Transactions on Applied Superconductivity",
issn = "1051-8223",
publisher = "Institute of Electrical and Electronics Engineers Inc.",
number = "2 PART III",

}

TY - JOUR

T1 - Magnetic-field properties of high critical current density YBCO films deposited by TFA-MOD

AU - Kim, Seok Beom

AU - Murase, S.

AU - Yamada, Y.

AU - Araki, T.

AU - Hirabayashi, I.

PY - 2005/6

Y1 - 2005/6

N2 - The critical current density, Jc, of metal-organic deposition process using trifluoroacetates (TFA-MOD) based YBCO films was measured between 20 K and 77 K in magnetic fields up to 9.5 T as a function of the field direction. C-axis oriented YBCO films was deposited on LaAlO3 single crystalline substrates and also on CeO2 buffered IBAD (YSZ/Hastelloy) substrates by TFA-MOD method. The obtained Jc values at 77 K and 0 T were 7 and 1.7 MA/cm2 for LaAlO3 and IBAD substrates, respectively. High Jc values over 105 A/cm2 were maintained up to 4 T (B//c-axis) for the LaAlO3 substrate and up to 3 T (B//c-axis) for the CeO2 buffered IBAD substrate. These results imply that TFA-MOD with simple fabrication process is very promising for the practical YBCO coated conductor. And the dependences on temperature and angular of the Jc at various external magnetic fields for some different thicknesses YBCO films was reported.

AB - The critical current density, Jc, of metal-organic deposition process using trifluoroacetates (TFA-MOD) based YBCO films was measured between 20 K and 77 K in magnetic fields up to 9.5 T as a function of the field direction. C-axis oriented YBCO films was deposited on LaAlO3 single crystalline substrates and also on CeO2 buffered IBAD (YSZ/Hastelloy) substrates by TFA-MOD method. The obtained Jc values at 77 K and 0 T were 7 and 1.7 MA/cm2 for LaAlO3 and IBAD substrates, respectively. High Jc values over 105 A/cm2 were maintained up to 4 T (B//c-axis) for the LaAlO3 substrate and up to 3 T (B//c-axis) for the CeO2 buffered IBAD substrate. These results imply that TFA-MOD with simple fabrication process is very promising for the practical YBCO coated conductor. And the dependences on temperature and angular of the Jc at various external magnetic fields for some different thicknesses YBCO films was reported.

KW - Jc - B - θ

KW - TFA-MOD

KW - Thickness

KW - YBCO film

UR - http://www.scopus.com/inward/record.url?scp=22044439596&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=22044439596&partnerID=8YFLogxK

U2 - 10.1109/TASC.2005.847757

DO - 10.1109/TASC.2005.847757

M3 - Article

AN - SCOPUS:22044439596

VL - 15

SP - 2645

EP - 2648

JO - IEEE Transactions on Applied Superconductivity

JF - IEEE Transactions on Applied Superconductivity

SN - 1051-8223

IS - 2 PART III

ER -