Hip Treatment on the Bi-Pb Oxide High-Tc Superconductor

Jun Takada, Hiroaki Asano, Hitoshi Kitaguchi, Kiichi Oda, Akiyoshi Osaka, Yoshinari Miura, Hiromasa Mazaki, Kazuyuki Shibutani, Rikuo Ogawa

Research output: Contribution to journalArticle

Abstract

It is well known that HIP treatment provides highly densified ceramics. The influences of HIP treatment on the densification of the Bi-Pb high-Tc ceramics and the electrical conductivity have been studied on the sample with a nominal composition of Bi0.96Pb0.24Sr1.0Ca1.1Cu1.6Ox. It was found that tlle density of the sample was attained over 90% of the theoretical density of the Bi-Pb high-Tc phase by the HIP treatment at 850°C for 2h. While the electrical resistance of the sample without HIP treatment decreased in linear with decreasing temperature from 280K to 120K and dropped to zero near 100K within the experimental limit, that of the HIP treated sample increased semiconductively between the temperature range from 280K to 110K, and below 110K gradually dropped to zero at 60-70K. However, the degradation of the HIP treated sample in the electrical conductivity was recovered by the heat treatment at 850°C for 48h in air. This behavior in the electrical conductivity seems to be associated with the precipitation of Ca2PbO4 in the grain boundary and the deficient of oxygen in the high-Tc phase.

Original languageEnglish
Pages (from-to)83-88
Number of pages6
JournalJournal of the Japan Society of Powder and Powder Metallurgy
Volume37
Issue number1
DOIs
Publication statusPublished - Jan 1 1990

ASJC Scopus subject areas

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Hip Treatment on the Bi-Pb Oxide High-Tc Superconductor'. Together they form a unique fingerprint.

  • Cite this

    Takada, J., Asano, H., Kitaguchi, H., Oda, K., Osaka, A., Miura, Y., Mazaki, H., Shibutani, K., & Ogawa, R. (1990). Hip Treatment on the Bi-Pb Oxide High-Tc Superconductor. Journal of the Japan Society of Powder and Powder Metallurgy, 37(1), 83-88. https://doi.org/10.2497/jjspm.37.83