Effects of Artificial Aging on Material Properties of Die-Cast Al–Si–Cu–Mg–xNa Alloy

Naoki Sahara, Reiya Ikeda, Shaohua Wu, Mitsuhiro Okayasu

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

The influence of sodium on the microstructural characteristics and mechanical properties of die-cast Al–Si–Cu–Mg (ADC12) alloy has been examined experimentally. Mechanical properties of the die-cast Al–Si–Cu–Mg alloy have increased with the addition of 0.03% Na, because of modification of the shape of the Si eutectic particles from acicular to fine and fibrous appearing. However, the mechanical properties decreased when 0.04% Na or more was added, due to the formation of shrinkage porosity. The fine and fibrous appearing eutectic Si has been created by the interruption of the nucleation and growth of Si eutectic by Na. The mechanical properties of Na containing die-cast ADC12 alloy were further enhanced by a T5 treating which is a low-temperature aging, giving rise to significant precipitation of fine CuAl2 and Mg2Si. In contrast, the mechanical properties of die-cast ADC12 T6-treated samples were lower due to the formation of blister defects. Thus, the solid solution process in the T6 treatment may not make severe precipitation hardening of die-cast ADC12 due to overaging. Moreover, severe precipitation hardening occurred by the artificial aging after microstructural refinement by Na.

Original languageEnglish
JournalInternational Journal of Metalcasting
DOIs
Publication statusAccepted/In press - 2022

Keywords

  • aluminum alloy
  • cast defects
  • die-casting
  • material
  • properties
  • sodium

ASJC Scopus subject areas

  • Mechanics of Materials
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Effects of Artificial Aging on Material Properties of Die-Cast Al–Si–Cu–Mg–xNa Alloy'. Together they form a unique fingerprint.

Cite this