Effect of reducing atmosphere on AIN ceramics sintered by millimerter Wave-HIP combined sintering

Kyohei Yamashita, Yoshihisa Kogo, Takasi Teranisi, Hidetaka Hayashi, Akira Kishimoto

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The effect of reducing atmosphere on yttria dispersed AIN ceramics sintered by millimeter wave-HIP combined sintering was investigated. The specimens were sintered by millimeter wave (MMW) heating under nitrogen reducing atmosphere containing 3 vol% hydrogen followed by post-HIP treatment at 1700°C for 0.5 h under nitrogen pressure of 190 MPa. The relative densities to the theoretical one saturated at the first MMW heating over 1700°C. Thermal conductivities of AIN ceramics sintered by MMW heating under heavily reduced atmosphere with nitrogen were higher than that through MMW heating under normally reduced atmosphere. The thermal conductivity increased with decreasing the yttria additive amount and with increasing the sintering temperature. The optimized yttria dispersion amount was 1 wt% in the MMW heating at 1800°C for 0.5 h. Relative density and thermal conductivity increased by post-HIP treatment. The optimized yttria dispersion amount shifted from 1 wt% to 3 wt% after post-HIP treatment.

Original languageEnglish
Pages (from-to)17-21
Number of pages5
JournalFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
Volume59
Issue number1
DOIs
Publication statusPublished - Jan 2012

Fingerprint

Hot isostatic pressing
Millimeter waves
Sintering
Yttrium oxide
Heating
Thermal conductivity
Nitrogen
Hydrogen
yttria

Keywords

  • AIN
  • Millimeter-wave heating
  • Post-HIP
  • Reducing atmosphere

ASJC Scopus subject areas

  • Industrial and Manufacturing Engineering
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

Effect of reducing atmosphere on AIN ceramics sintered by millimerter Wave-HIP combined sintering. / Yamashita, Kyohei; Kogo, Yoshihisa; Teranisi, Takasi; Hayashi, Hidetaka; Kishimoto, Akira.

In: Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, Vol. 59, No. 1, 01.2012, p. 17-21.

Research output: Contribution to journalArticle

@article{c5e0377882bf4bb9ab60bd3fbc92c90f,
title = "Effect of reducing atmosphere on AIN ceramics sintered by millimerter Wave-HIP combined sintering",
abstract = "The effect of reducing atmosphere on yttria dispersed AIN ceramics sintered by millimeter wave-HIP combined sintering was investigated. The specimens were sintered by millimeter wave (MMW) heating under nitrogen reducing atmosphere containing 3 vol{\%} hydrogen followed by post-HIP treatment at 1700°C for 0.5 h under nitrogen pressure of 190 MPa. The relative densities to the theoretical one saturated at the first MMW heating over 1700°C. Thermal conductivities of AIN ceramics sintered by MMW heating under heavily reduced atmosphere with nitrogen were higher than that through MMW heating under normally reduced atmosphere. The thermal conductivity increased with decreasing the yttria additive amount and with increasing the sintering temperature. The optimized yttria dispersion amount was 1 wt{\%} in the MMW heating at 1800°C for 0.5 h. Relative density and thermal conductivity increased by post-HIP treatment. The optimized yttria dispersion amount shifted from 1 wt{\%} to 3 wt{\%} after post-HIP treatment.",
keywords = "AIN, Millimeter-wave heating, Post-HIP, Reducing atmosphere",
author = "Kyohei Yamashita and Yoshihisa Kogo and Takasi Teranisi and Hidetaka Hayashi and Akira Kishimoto",
year = "2012",
month = "1",
doi = "10.2497/jjspm.59.17",
language = "English",
volume = "59",
pages = "17--21",
journal = "Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy",
issn = "0532-8799",
publisher = "Funtai Funamtsu Yakin Kyokai/Japan Soc. of Powder Metallurgy",
number = "1",

}

TY - JOUR

T1 - Effect of reducing atmosphere on AIN ceramics sintered by millimerter Wave-HIP combined sintering

AU - Yamashita, Kyohei

AU - Kogo, Yoshihisa

AU - Teranisi, Takasi

AU - Hayashi, Hidetaka

AU - Kishimoto, Akira

PY - 2012/1

Y1 - 2012/1

N2 - The effect of reducing atmosphere on yttria dispersed AIN ceramics sintered by millimeter wave-HIP combined sintering was investigated. The specimens were sintered by millimeter wave (MMW) heating under nitrogen reducing atmosphere containing 3 vol% hydrogen followed by post-HIP treatment at 1700°C for 0.5 h under nitrogen pressure of 190 MPa. The relative densities to the theoretical one saturated at the first MMW heating over 1700°C. Thermal conductivities of AIN ceramics sintered by MMW heating under heavily reduced atmosphere with nitrogen were higher than that through MMW heating under normally reduced atmosphere. The thermal conductivity increased with decreasing the yttria additive amount and with increasing the sintering temperature. The optimized yttria dispersion amount was 1 wt% in the MMW heating at 1800°C for 0.5 h. Relative density and thermal conductivity increased by post-HIP treatment. The optimized yttria dispersion amount shifted from 1 wt% to 3 wt% after post-HIP treatment.

AB - The effect of reducing atmosphere on yttria dispersed AIN ceramics sintered by millimeter wave-HIP combined sintering was investigated. The specimens were sintered by millimeter wave (MMW) heating under nitrogen reducing atmosphere containing 3 vol% hydrogen followed by post-HIP treatment at 1700°C for 0.5 h under nitrogen pressure of 190 MPa. The relative densities to the theoretical one saturated at the first MMW heating over 1700°C. Thermal conductivities of AIN ceramics sintered by MMW heating under heavily reduced atmosphere with nitrogen were higher than that through MMW heating under normally reduced atmosphere. The thermal conductivity increased with decreasing the yttria additive amount and with increasing the sintering temperature. The optimized yttria dispersion amount was 1 wt% in the MMW heating at 1800°C for 0.5 h. Relative density and thermal conductivity increased by post-HIP treatment. The optimized yttria dispersion amount shifted from 1 wt% to 3 wt% after post-HIP treatment.

KW - AIN

KW - Millimeter-wave heating

KW - Post-HIP

KW - Reducing atmosphere

UR - http://www.scopus.com/inward/record.url?scp=84880524928&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84880524928&partnerID=8YFLogxK

U2 - 10.2497/jjspm.59.17

DO - 10.2497/jjspm.59.17

M3 - Article

AN - SCOPUS:84880524928

VL - 59

SP - 17

EP - 21

JO - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

JF - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy

SN - 0532-8799

IS - 1

ER -