Effect of Pretreatment and Activation Mode on the Interfacial Adaptation of Nanoceramic Resin Inlay and Self-adhesive Resin Cement

Seung Hoon Han, Yasushi Shimada, Alireza Sadr, Junji Tagami, Kee Yeon Kum, Sung Ho Park

Research output: Contribution to journalArticlepeer-review

3 Citations (Scopus)

Abstract

Objectives: The first objective of this study was to determine if the luting material used for resin nanoceramic inlay affects interfacial adaptation. The second was to investigate whether pretreatment and the adhesive curing method before cementation affects interfacial adaptation. The final objective was to compare activation modes of luting material. Methods: Class I cavities were prepared on extracted human third molars. Resin nanoceramic inlays were fabricated using Lava Ultimate CAD/CAM block (3 M). For the control groups, inlays were cemented using Panavia V5 (Kuraray Noritake). For the experimental groups, teeth were randomly divided into five experimental groups with four subgroups using different self-adhesive cements (SACs). Cement in Group I was dual-cured without pretreatment. In Group II, the cement was dual-cured after polyacrylic acid treatment of the tooth cavity. In Groups III and IV, the cement was dual-cured after universal dentin adhesive treatment with pre-cure and co-cure methods. In Group V, the inlay was cemented in self-cure mode. After thermocycling, interfacial adaptation at the inlay-tooth interface was measured using swept-source optical coherence tomography (SS-OCT) imaging. Finally, polymerization shrinkage strain of the luting material was measured and compared. Results: Interfacial adaptation differed depending on the luting material. After application of a universal adhesive, some subgroups showed improved interfacial adaptation. Interfacial adaptation and polymerization shrinkage strain differed significantly depending on activation mode. Significance: Interfacial adaptation for a resin nanoceramic inlay can differ according to the type of SAC and activation mode. For some SACs, application of a universal adhesive before cementation improves interfacial adaptation.

Original languageEnglish
Pages (from-to)1170-1182
Number of pages13
JournalDental Materials
Volume36
Issue number9
DOIs
Publication statusPublished - Sep 2020

Keywords

  • activation mode
  • interfacial adaptation
  • nanoceramic resin inlay
  • pretreatment
  • self-adhesive resin cement
  • self-curing potential

ASJC Scopus subject areas

  • Materials Science(all)
  • Dentistry(all)
  • Mechanics of Materials

Fingerprint Dive into the research topics of 'Effect of Pretreatment and Activation Mode on the Interfacial Adaptation of Nanoceramic Resin Inlay and Self-adhesive Resin Cement'. Together they form a unique fingerprint.

Cite this