TY - JOUR
T1 - Effect of Ba Addition to the High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System (V)
AU - Yoshihiro, Kusano
AU - Kazuhiro, Yamaguchi
AU - Minoru, Fukuhara
AU - Akira, Doi
AU - Toshio, Takada
AU - Masashi, Fujiwara
AU - Jun, Takada
N1 - Copyright:
Copyright 2018 Elsevier B.V., All rights reserved.
PY - 1992
Y1 - 1992
N2 - The effects of cooling condition and Ba addition time on Tc of high-Tc phase in the Bi-Pb-Sr-Ca-Cu-O system were studied. X-ray diffraction and DC resistance measurements were carried out to observe phase identification and Tc values for a series of samples with compositions of Bi:Pb:Sr:Ba:Ca:Cu=0.9:0.2:1.0:X:1.0:1.6(X=0-0.05). When a mixture of BaCO3 and synthesized high-Tc phase was heated at 850°C for 60h in air, only a solid solution of high-Tc phase was formed in a quenched sample. However, in a sample cooled down slowly, Bi3(Sr, Ba)4Ca3Oz was found as an impurity phase in addition to the solid solution of high-Tc phase. Mixtures of BaCO3 (X=0.04) and the rest of metal oxides or metal carbonates were heated at 845°C 96h in air. Bi3(Sr, Ba)4Ca3Oz was also found in addition to the high-Tc phase in a quenched sample. When BaCO3 was added to the synthesized high-Tc phase, Tc(R=0) was 119K for the heated samples. When BaCO3 was added in starting materials, Tc decreased to 110K due to the formation of Bi3(Sr, Ba)4Ca3OZ.
AB - The effects of cooling condition and Ba addition time on Tc of high-Tc phase in the Bi-Pb-Sr-Ca-Cu-O system were studied. X-ray diffraction and DC resistance measurements were carried out to observe phase identification and Tc values for a series of samples with compositions of Bi:Pb:Sr:Ba:Ca:Cu=0.9:0.2:1.0:X:1.0:1.6(X=0-0.05). When a mixture of BaCO3 and synthesized high-Tc phase was heated at 850°C for 60h in air, only a solid solution of high-Tc phase was formed in a quenched sample. However, in a sample cooled down slowly, Bi3(Sr, Ba)4Ca3Oz was found as an impurity phase in addition to the solid solution of high-Tc phase. Mixtures of BaCO3 (X=0.04) and the rest of metal oxides or metal carbonates were heated at 845°C 96h in air. Bi3(Sr, Ba)4Ca3Oz was also found in addition to the high-Tc phase in a quenched sample. When BaCO3 was added to the synthesized high-Tc phase, Tc(R=0) was 119K for the heated samples. When BaCO3 was added in starting materials, Tc decreased to 110K due to the formation of Bi3(Sr, Ba)4Ca3OZ.
UR - http://www.scopus.com/inward/record.url?scp=85004455835&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85004455835&partnerID=8YFLogxK
U2 - 10.2497/jjspm.39.374
DO - 10.2497/jjspm.39.374
M3 - Article
AN - SCOPUS:85004455835
VL - 39
SP - 374
EP - 377
JO - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
JF - Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
SN - 0532-8799
IS - 5
ER -