Change of electrical resistivity with martensite transformation of Ti-42 mass%Nb alloy

Yoshito Takemoto, Takuya Maruyama, Masataka Ijiri

Research output: Contribution to journalArticle

Abstract

The behavior of the martensite transformation of Ti42 mass%Nb alloy was investigated by electrical resistivity measurement. The β phase was fully retained upon quenching from 1050℃. In the cooling and heating process below room temperature, hysteresis due to the martensite transformation was clearly observed, in contrast to previously reported behavior. The MS and Af temperatures of the sample prepared from the outer layer of a quenched plate were lower than those of the inner layer. Treatment of the solution under a low vacuum condition also lowered these temperatures and the hysteresis loop became much smaller. The effect of the solution temperature above βtransus on the transformation behavior was negligible. By heating to 400℃, the whole resistivity curve shifted upward, and the ωS temperature increased, but the hysteresis loop still appeared at a low temperature. In situ TEM observation revealed that acicular martensite was formed at a low temperature and disappeared with heating, and that the reflection intensities of ω and α" in the β matrix increased with cooling. However, such behavior was hardly observed in a region irradiated by an electron beam during cooling.

Original languageEnglish
Pages (from-to)256-261
Number of pages6
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume82
Issue number7
DOIs
Publication statusPublished - Jan 1 2018

Keywords

  • Hysteresis
  • Impurity
  • MS point
  • Sampling
  • Solution treatment
  • Α”-martensite
  • Ω-phase

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Change of electrical resistivity with martensite transformation of Ti-42 mass%Nb alloy'. Together they form a unique fingerprint.

  • Cite this