Analysis of microstructural effects on mechanical properties of copper alloys

Mitsuhiro Okayasu, Takuya Muranaga, Ayana Endo

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

With the aim of obtaining copper alloys with favorable mechanical properties (high strength and high ductility) for various engineering applications, the microstructural characteristics of two conventional copper alloys — an aluminum bronze (AlBC; Cu–Al9.3–Fe3.8–Ni2–Mn0.8) and a brass (HB: Cu–Al4–Zn25–Fe3–Mn3.8) — and a recently developed aluminum bronze (CADZ: Cu–Al10.5–Fe3.1–Ni3.5–Mn1.1–Sn3.7), were controlled by subjecting the alloys to two different processes (rolling and casting) under various conditions. For the rolling process, the rolling rate and temperature were varied, whereas for the casting process, the solidification rate was varied. Microstructural characteristics, as examined by electron backscatter diffraction analysis, were found to differ among the alloys. Complicated microstructures formed in CADZ led to high hardness and high tensile strength (σUTS), but low ductility (εf). For CADZ, casting at a high solidification rate allowed an increase in ductility to be obtained as a result of fine-grained structure and low internal stress. In contrast, high ductility (with a fracture strain of more than 30%) was found for both cast AlBC and cast HB; moreover, both of these alloys possessed high tensile strength when produced by warm rolling at 473 K. For CADZ, on the other hand, no clear effect of rolling on tensile strength could be found, owing to the many microcracks caused by its brittleness. The results of this study indicate that copper alloys with excellent mechanical properties can be produced. This is especially the case for the conventional alloys, with a high tensile strength σUTS = 900 MPa and a high fracture strain εf = 10% being obtained for warm-rolled brass.

Original languageEnglish
Pages (from-to)128-139
Number of pages12
JournalJournal of Science: Advanced Materials and Devices
Volume2
Issue number1
DOIs
Publication statusPublished - Mar 1 2017

Fingerprint

Copper alloys
Ductility
Tensile strength
Mechanical properties
Casting
Bronze
Solidification
Brass
Aluminum copper alloys
Microcracks
Brittleness
Aluminum
Electron diffraction
Residual stresses
Hardness
Microstructure
Temperature
brass

Keywords

  • Brass
  • Bronze
  • Ductility
  • Microstructural characteristics
  • Strength

ASJC Scopus subject areas

  • Ceramics and Composites
  • Biomaterials
  • Electronic, Optical and Magnetic Materials
  • Materials Science (miscellaneous)

Cite this

Analysis of microstructural effects on mechanical properties of copper alloys. / Okayasu, Mitsuhiro; Muranaga, Takuya; Endo, Ayana.

In: Journal of Science: Advanced Materials and Devices, Vol. 2, No. 1, 01.03.2017, p. 128-139.

Research output: Contribution to journalArticle

@article{f172958d90af4e8fafd8bd9dea64757c,
title = "Analysis of microstructural effects on mechanical properties of copper alloys",
abstract = "With the aim of obtaining copper alloys with favorable mechanical properties (high strength and high ductility) for various engineering applications, the microstructural characteristics of two conventional copper alloys — an aluminum bronze (AlBC; Cu–Al9.3–Fe3.8–Ni2–Mn0.8) and a brass (HB: Cu–Al4–Zn25–Fe3–Mn3.8) — and a recently developed aluminum bronze (CADZ: Cu–Al10.5–Fe3.1–Ni3.5–Mn1.1–Sn3.7), were controlled by subjecting the alloys to two different processes (rolling and casting) under various conditions. For the rolling process, the rolling rate and temperature were varied, whereas for the casting process, the solidification rate was varied. Microstructural characteristics, as examined by electron backscatter diffraction analysis, were found to differ among the alloys. Complicated microstructures formed in CADZ led to high hardness and high tensile strength (σUTS), but low ductility (εf). For CADZ, casting at a high solidification rate allowed an increase in ductility to be obtained as a result of fine-grained structure and low internal stress. In contrast, high ductility (with a fracture strain of more than 30{\%}) was found for both cast AlBC and cast HB; moreover, both of these alloys possessed high tensile strength when produced by warm rolling at 473 K. For CADZ, on the other hand, no clear effect of rolling on tensile strength could be found, owing to the many microcracks caused by its brittleness. The results of this study indicate that copper alloys with excellent mechanical properties can be produced. This is especially the case for the conventional alloys, with a high tensile strength σUTS = 900 MPa and a high fracture strain εf = 10{\%} being obtained for warm-rolled brass.",
keywords = "Brass, Bronze, Ductility, Microstructural characteristics, Strength",
author = "Mitsuhiro Okayasu and Takuya Muranaga and Ayana Endo",
year = "2017",
month = "3",
day = "1",
doi = "10.1016/j.jsamd.2016.12.003",
language = "English",
volume = "2",
pages = "128--139",
journal = "Journal of Science: Advanced Materials and Devices",
issn = "2468-2284",
publisher = "Elsevier BV",
number = "1",

}

TY - JOUR

T1 - Analysis of microstructural effects on mechanical properties of copper alloys

AU - Okayasu, Mitsuhiro

AU - Muranaga, Takuya

AU - Endo, Ayana

PY - 2017/3/1

Y1 - 2017/3/1

N2 - With the aim of obtaining copper alloys with favorable mechanical properties (high strength and high ductility) for various engineering applications, the microstructural characteristics of two conventional copper alloys — an aluminum bronze (AlBC; Cu–Al9.3–Fe3.8–Ni2–Mn0.8) and a brass (HB: Cu–Al4–Zn25–Fe3–Mn3.8) — and a recently developed aluminum bronze (CADZ: Cu–Al10.5–Fe3.1–Ni3.5–Mn1.1–Sn3.7), were controlled by subjecting the alloys to two different processes (rolling and casting) under various conditions. For the rolling process, the rolling rate and temperature were varied, whereas for the casting process, the solidification rate was varied. Microstructural characteristics, as examined by electron backscatter diffraction analysis, were found to differ among the alloys. Complicated microstructures formed in CADZ led to high hardness and high tensile strength (σUTS), but low ductility (εf). For CADZ, casting at a high solidification rate allowed an increase in ductility to be obtained as a result of fine-grained structure and low internal stress. In contrast, high ductility (with a fracture strain of more than 30%) was found for both cast AlBC and cast HB; moreover, both of these alloys possessed high tensile strength when produced by warm rolling at 473 K. For CADZ, on the other hand, no clear effect of rolling on tensile strength could be found, owing to the many microcracks caused by its brittleness. The results of this study indicate that copper alloys with excellent mechanical properties can be produced. This is especially the case for the conventional alloys, with a high tensile strength σUTS = 900 MPa and a high fracture strain εf = 10% being obtained for warm-rolled brass.

AB - With the aim of obtaining copper alloys with favorable mechanical properties (high strength and high ductility) for various engineering applications, the microstructural characteristics of two conventional copper alloys — an aluminum bronze (AlBC; Cu–Al9.3–Fe3.8–Ni2–Mn0.8) and a brass (HB: Cu–Al4–Zn25–Fe3–Mn3.8) — and a recently developed aluminum bronze (CADZ: Cu–Al10.5–Fe3.1–Ni3.5–Mn1.1–Sn3.7), were controlled by subjecting the alloys to two different processes (rolling and casting) under various conditions. For the rolling process, the rolling rate and temperature were varied, whereas for the casting process, the solidification rate was varied. Microstructural characteristics, as examined by electron backscatter diffraction analysis, were found to differ among the alloys. Complicated microstructures formed in CADZ led to high hardness and high tensile strength (σUTS), but low ductility (εf). For CADZ, casting at a high solidification rate allowed an increase in ductility to be obtained as a result of fine-grained structure and low internal stress. In contrast, high ductility (with a fracture strain of more than 30%) was found for both cast AlBC and cast HB; moreover, both of these alloys possessed high tensile strength when produced by warm rolling at 473 K. For CADZ, on the other hand, no clear effect of rolling on tensile strength could be found, owing to the many microcracks caused by its brittleness. The results of this study indicate that copper alloys with excellent mechanical properties can be produced. This is especially the case for the conventional alloys, with a high tensile strength σUTS = 900 MPa and a high fracture strain εf = 10% being obtained for warm-rolled brass.

KW - Brass

KW - Bronze

KW - Ductility

KW - Microstructural characteristics

KW - Strength

UR - http://www.scopus.com/inward/record.url?scp=85032207883&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85032207883&partnerID=8YFLogxK

U2 - 10.1016/j.jsamd.2016.12.003

DO - 10.1016/j.jsamd.2016.12.003

M3 - Article

AN - SCOPUS:85032207883

VL - 2

SP - 128

EP - 139

JO - Journal of Science: Advanced Materials and Devices

JF - Journal of Science: Advanced Materials and Devices

SN - 2468-2284

IS - 1

ER -