Accelerated tests on Si and SiC power transistors with thermal, fastand ultra-fast neutrons

Fabio Principato, Saverio Altieri, Leonardo Abbene, Francesco Pintacuda

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

Neutron test campaigns on silicon (Si) and silicon carbide (SiC) power MOSFETs and IGBTs were conducted at the TRIGA (Training, Research, Isotopes, General Atomics) Mark II (Pavia, Italy) nuclear reactor and ChipIr-ISIS Neutron and Muon Source (Didcot, U.K.) facility. About 2000 power transistors made by STMicroelectronics were tested in all the experiments. Tests with thermal and fast neutrons (up to about 10 MeV) at the TRIGA Mark II reactor showed that single-event burnout (SEB) failures only occurred at voltages close to the rated drain-source voltage. Thermal neutrons did not induce SEB, nor degradation in the electrical parameters of the devices. SEB failures during testing at ChipIr with ultra-fast neutrons (1-800 MeV) were evaluated in terms of failure in time (FIT) versus derating voltage curves according to the JEP151 procedure of the Joint Electron Device Engineering Council (JEDEC). These curves, even if scaled with die size and avalanche voltage, were strongly linked to the technological processes of the devices, although a common trend was observed that highlighted commonalities among the failures of different types of MOSFETs. In both experiments, we observed only SEB failures without single-event gate rupture (SEGR) during the tests. None of the power devices that survived the neutron tests were degraded in their electrical performances. A study of the worst-case bias condition (gate and/or drain) during irradiation was performed.

Original languageEnglish
Article number3021
JournalSensors (Switzerland)
Volume20
Issue number11
DOIs
Publication statusPublished - Jun 1 2020
Externally publishedYes

Keywords

  • Failure in time
  • Neutron beams
  • Power device reliability
  • Silicon carbide
  • Single-event burnout

ASJC Scopus subject areas

  • Analytical Chemistry
  • Biochemistry
  • Atomic and Molecular Physics, and Optics
  • Instrumentation
  • Electrical and Electronic Engineering

Fingerprint

Dive into the research topics of 'Accelerated tests on Si and SiC power transistors with thermal, fastand ultra-fast neutrons'. Together they form a unique fingerprint.

Cite this